Surface modification of anhydrous borax with stearic acid by wet coating method

• Authors Details :  
• Cansu Kurtulus,  
• Recep Kurtulus

Journal title : JOURNAL OF CHARACTERIZATION

Publisher : ASOS Yayinevi

Online ISSN : 2757-9166

Page Number : 1-9

Journal volume : 1

Journal issue : 1

811 Views Research reports

The wet coating of anhydrous borax powders with stearic acid (SA) to reverse their inherent hydrophilic surface properties was investigated. The coating procedure was based on the results from a previous study that revealed that the stearic acid solution (2 wt. % SA) mixed for 60 minute at 750 rpm on the magnetic stirrer was sufficient for the surface modification of anhydrous borax. For the experiments, stearic acid powders were first dissolved in water at 80 °C. The mixture obtained by adding anhydrous borax powders to this solution was vigorously mixed on a magnetic stirrer to initiation and completion the surface modification. Each of these solutions was then filtered using a filter paper to separate the undissolved particles, and the residue on paper was dried at 50 °C for 48 h until constant weighing was obtained. Wettability has been accepted as a key parameter for success in wet coating treatment. This parameter gained via the experimental characterization technique was used for an evaluation of the powder properties. The degree of wettability of anhydrous borax powders was measured and compared both after their surfaces were coated with stearic acid and after they were treated with water for a certain period of time in an aqueous environment. The stearic acid coating made the powder hydrophobic and this property was highly preserved after washing.

Article DOI & Crossmark Data

DOI : https://doi.org/10.29228/JCAR.1

Article Subject Details

• Materials Science

Article Keywords Details

• Anhydrous borax
• Solubility
• Stearic acid
• Wet Coating
• Surface modification

Article File

Full Text PDF

---

---

---

More Article by Journal of Characterization